High Quality GI SECC DX51 Z90 Z100 Z125 ZINC Coated Galvanized Metals Coil
| Item name | SGCC HDGI gi coil z90 z120 hot dipped galvanized steel coils | ||
| Grade | DX51D+Z | S250GD+Z | |
| SGCC | DX52D+Z | S280GD+Z | |
| SGCD | DX53D+Z | S350GD+Z | |
| SGCE | DX54D+Z | S550GD+Z | |
| DX56D+Z | |||
| Thickness | 0.12 ~ 3.00 mm (cold rolled) | ||
| 1.20 ~ 4.60 mm (Hot-rolled ) | |||
| Width | 10 - 600 mm (strip) | ||
| 600 - 1250 mm (coil) | |||
| Tolerance | Thickness: ±0.01 mm | ||
| Width: ±2 mm | |||
| Coil ID | 508 mm - 610 mm | ||
| Coil weight | 3 - 8 ton or as client requirement. | ||
| Zinc coating | 30g - 275g / m2 | ||
| Spangle | Big spangle,Regular spangle,Mini spangle,Zero spangle | ||
| Surface treatment | Oil,Passivation, Chromated, Skin-passed, Anti-finger Print | ||
| HS code | code 72104900 | ||
| Application | Widely used in road, railway, civil construction, water conservancy construction; all kinds of machinery, electrical appliances, window protection and aquaculture, etc. | ||
| Package | Standard export package (Plastic film in the first layer,second layer is Kraft paper. Third layer is galvanized sheet) | ||
| Delivery time | Within 15 workdays after deposit received | ||
| Remarks | Insurance per to Contract terms; MTC will be handed on with shipping documents; We accept the third party certificatation test. | ||
| STEEL GRADE | CHEMICAL COMPOSITION % | MECHANIC PROPERTY | C.B OF | COATING | ||||||
| C | Si | Mn | S | P | T.S | Y.S | E.L | COATING | ||
| x103 | x103 | x102 | x103 | x103 | Mpa | Mpa | % | d=0 180° | G/M² | |
| JIS G3302 SGCC | 12 | 30 | 41 | 31 | 21 | 480 | 300 | 13 | OK | Z60-150 |
| JIS G3302 SGCH | 12 | 10 | 21 | 18 | 8 | 680 | 650 | 20 | OK | Z60-150 |
| ASTM A653 CS.B | 29 | 30 | 60 | 35 | 30 | 386 | 250-380 | 20 | OK | Z60-275 |
| DX51D+Z | 20 | 21 | 18 | 1.8 | 11 | 355 | 245 | 38 | OK | Z60-275 |
Product details
Hot-dip galvanizing is the reaction of molten metal with an iron substrate to produce an alloy layer, thereby combining the substrate and the plating layer. Hot-dip galvanizing is to pickle iron and steel parts first. In order to remove iron oxide on the surface of iron and steel parts, after pickling, it is cleaned in an ammonium chloride or zinc chloride aqueous solution or a mixed solution of ammonium chloride and zinc chloride.And then sent to the hot-dip plating bath. Hot-dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.